JIS G3456 YEES YOG DAB
Jis G3456 Txheem qhia meej cov cai rau cov roj txheem hluav taws xob rau kev siv cov pa dej siab, thiab siv cov kev mob ntawm sab nraud ntawm 10.5 hli thiab 660.4 hli. Cov kav dej hlau no tau npaj rau kev siv ntawm qhov kub tshaj ntawm 350 degree thiab feem ntau yog siv hauv cov pa luam yeeb kub. Tus qauv tau tsim los xyuas kom cov kev ua tau zoo thiab kev nyab xeeb ntawm cov kav hlau loj hauv ib puag ncig kub.
JIS G3456 Cov kav dej hlau muaj nyob rau ntau yam qhab nia, suav nrog: stpt 370, stpt 410, stpt 480, thiab lwm tus.
Stet 370 tshuaj lom neeg (%)
| muaj pes tsawg | C | Si | Mn | P | S |
|---|---|---|---|---|---|
| Lub min | - | 0.1 | 0.3 | - | - |
| Tus zuag | 0.25 | 0.35 | 0.9 | 0.035 | 0.035 |
Stt 370 cov khoom siv mechanical
| Lub zog tensile σb MPa |
Paib σs MPa |
Elongation thaum tawg lossis elongationδδδ % |
|---|---|---|
| Ntau dua los yog sib npaug rau 370 | Ntau dua los yog sib npaug rau 215 | ntev. Ntau dua los yog sib npaug rau 30 © Ntau dua los yog sib npaug rau 28® Ntau dua los yog sib npaug rau 24 * tr. Ntau dua los yog sib npaug rau 25 ※ Ntau dua los yog sib npaug rau 23® Ntau dua los yog sib npaug rau 20 * |
Stpt 410 tshuaj lom neeg muaj pes tsawg leeg (%)
| muaj pes tsawg | C | Si | Mn | P | S |
|---|---|---|---|---|---|
| Lub min | - | 0.1 | 0.3 | - | - |
| Tus zuag | 0.3 | 0.35 | 1 | 0.035 | 0.035 |
Stp 410 cov neeg kho tshuab khoom siv
| Lub zog tensile σb MPa |
Paib σs MPa |
Elongation thaum tawg lossis elongationδδδ δ % |
|---|---|---|
| Ntau dua los yog sib npaug rau 410 | Ntau dua los yog sib npaug rau 245 | ntev. Ntau dua los yog sib npaug rau 25 © Ntau dua los yog sib npaug rau 24® Ntau dua los yog sib npaug rau 21 * tr. Ntau dua los yog sib npaug rau 20 ※ Ntau dua los yog sib npaug rau 19® Ntau dua los yog sib luag rau 17 * |
Stpt 480 cov khoom siv tshuaj (%)
| muaj pes tsawg | C | Si | Mn | P | S |
|---|---|---|---|---|---|
| Lub min | - | 0.1 | 0.3 | - | - |
| Tus zuag | 0.33 | 0.35 | 1 | 0.035 | 0.035 |
Stpt 480 cov khoom siv mecha kho tshuab
| Lub zog tensile σb MPa |
Paib σs MPa |
Elongation thaum tawg lossis elongationδδδ δ % |
|---|---|---|
| Ntau dua los yog sib npaug rau 480 | Ntau dua los yog sib npaug rau 275 | ntev. Ntau dua los yog sib npaug rau 25 © Ntau dua los yog sib npaug rau 22® Ntau dua los yog sib npaug rau 19 * tr. Ntau dua los yog sib npaug rau 20 ※ Ntau dua los yog sib npaug rau 17® Ntau dua los yog sib npaug rau 15 * |